| Place of Origin: | CHINA |
|---|---|
| Brand Name: | BAO STEEL |
| Certification: | ISO,SGS, CE, RoSH |
| Model Number: | ASME SA516 Grade 70 |
| Minimum Order Quantity: | 10 Tons |
| Price: | Negotiation |
| Packaging Details: | AS REQUIRED |
| Delivery Time: | 5-15 DAYS |
| Payment Terms: | L/C, T/T |
| Supply Ability: | 1000Tons per month |
| Length: | As Requirement | Width: | 600-2000mm |
|---|---|---|---|
| Thickness: | 3-200mm | Surface: | Oil,black,galvanized |
| Packing: | Standard Seaport Packing | Standard: | GB , JIS, ASTM , AISI , DIN |
| Material: | ASTM A36 | Technique: | Hot Rolled |
| High Light: | galvanized High Carbon Steel Sheet,30mm Q235 Carbon Steel Sheet,ASTM A36 High Carbon Steel Sheet |
||
|
Steel grade type
|
ASTM A36/Q235
|
|---|---|
|
Standard
|
|
|
Production specifications
|
Steel plate,Sheet, Coil,Flat bar,Round bar, Strip steel,wire,All kinds of forgings.
|
|
Mchining
|
Turning
Milling Grinding Deep hole drilling: length max 9.8 meters. |
|
Range of work
|
Round bar steel: 1mm to 2000mm
Square-shape steel: 10mm to 1000mm
steel Plate/sheet:0.08mm to 800mm
Width: 10mm to 1500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ4-410 mm, with wall thickness ranging from 1-35 mm.
|
|
Heat treatment
|
Normalizing,Annealing,Tempering,Quenching,Hardening and tempering,Seasoning,Surface hardening,Carburizing
|
|
Physical Properties
|
Metric
|
English
|
Comments
|
|---|---|---|---|
|
Density
|
7.85 g/cc
|
0.284 lb/in³
|
Typical of ASTM steel
|
|
|
|||
|
Mechanical Properties
|
Metric
|
English
|
Comments
|
|
Hardness, Brinell
|
119 - 159
|
119 - 159
|
based on conversion from tensile strength
|
|
Hardness, Rockwell B
|
67.0 - 83.0
|
67.0 - 83.0
|
based on conversion from tensile strength
|
|
Tensile Strength at Break
|
400 - 552 MPa
|
58000 - 80000 psi
|
|
|
Tensile Strength, Yield
|
>= 221 MPa
|
>= 32000 psi
|
|
|
Elongation at Break
|
>= 18.0 %
|
>= 18.0 %
|
in 8"
|
|
|
>= 21.0 %
|
>= 21.0 %
|
in 2", > 24" W
|
|
Bend Radius, Minimum
|
0.500 t
|
0.500 t
|
≤3/4" W; ASTM A6 PARA. S14
|
|
|
1.00 t
|
1.00 t
|
>3/4 to 1" W; ASTM A6 PARA. S14
|
|
|
1.50 t
|
1.50 t
|
>1 to 1-1/2" W; ASTM A6 PARA. S14
|
|
|
2.50 t
|
2.50 t
|
>1-1/2 to 2" W; ASTM A6 PARA. S14
|
|
|
3.00 t
|
3.00 t
|
>2" W; ASTM A6 PARA. S14
|
|
Properties
|
Conditions
|
||
|---|---|---|---|
|
T (°C)
|
Treatment
|
||
|
Density (×1000 kg/m3)
|
7.7-8.03
|
25
|
|
|
Poisson's Ratio
|
0.27-0.30
|
25
|
|
|
Elastic Modulus (GPa)
|
190-210
|
25
|
|
|
Tensile Strength (Mpa)
|
1158
|
25
|
oil quenched, fine grained, tempered at 425°C
|
|
Yield Strength (Mpa)
|
1034
|
||
|
Elongation (%)
|
15
|
||
|
Reduction in Area (%)
|
53
|
||
|
Hardness (HB)
|
335
|
25
|
oil quenched, fine grained, tempered at 425°C
|
|
Quantity
|
Value
|
Unit
|
|---|---|---|
|
Thermal expansion
|
16 - 17
|
e-6/K
|
|
Thermal conductivity
|
16 - 16
|
W/m.K
|
|
Specific heat
|
500 - 500
|
J/kg.K
|
|
Melting temperature
|
1370 - 1400
|
°C
|
|
Service temperature
|
0 - 500
|
°C
|
|
Density
|
8000 - 8000
|
kg/m3
|
|
Resistivity
|
0.7 - 0.7
|
Ohm.mm2/m
|