• Wuxi Jinlai Mechanical Processing Co., Ltd.
    John Fairbank
    stainless steel strip with good quality and the Sales clerk service is very good.i like this company i hope can work with your again
  • Wuxi Jinlai Mechanical Processing Co., Ltd.
    Fleuriau
    Shipment speed is very fast, and the requirements can meet me. Salesman is very responsible.
  • Wuxi Jinlai Mechanical Processing Co., Ltd.
    Fierce Urchin
    good ,the galvanized steel coil quality is good and i donot see the broken on them.that is nice
Contact Person : Jo Yuan
Phone Number : +86-18706170710
WhatsApp : +8618706170710

Multiple Grade ASTM A282 Cr Sheet Metal Flat Rolled Intermediate Tensile Strength

Place of Origin: China
Brand Name: JIN LAI
Certification: ISO BV
Model Number: ASME SA516 Grade 70
Minimum Order Quantity: 1 tons
Price: negotiation
Packaging Details: standard packing or as the requirement
Delivery Time: ship withon 10 days after receive the advance
Payment Terms: T/T, Western Union
Supply Ability: 5000 tons per month
Product Details
Length: As Requirement Surface: Oil,black,galvanized
Packing: Standard Seaport Packing Width: 600-2000mm
Standard: AISI, ASTM, BS, DIN, GB, JIS Material: ASTM A36
Thickness: 0.3-200mm Technique: Hot Rolled
High Light:

cold rolled mild steel sheet

,

carbon sheet metal

Leave a Message
Product Description

ASTM A283 Carbon Steel Plate

  • Grade: A B C D
  • Thickness: from 6mm to 150mm
  • Width: from 1,500mm to 4,100mm
  • Length: from 6,000mm to 20,000mm
  • ASTM A36, ASTM A572, ASTM A656, JIS G3101 SS400, EN10025-2, DIN 17100, DIN 17102, GB/T700, GB/T1591
  • ASTM A283 plate steel features low and intermediate tensile strength carbon steel plate of structural quality. It has four common variants, each represented as a separate material. The material properties section below shows ranges encompassing all variants.
  • This specification covers four grades of carbon steel plates of structural quality for general application. Steel samples shall be melt processed by either open-hearth, basic-oxygen, or electric furnace. Heat and product analysis shall be performed wherein steel materials shall conform to required chemical compositions of carbon, manganese, phosphorus, sulfur, silicon, and copper. Steel specimens shall also undergo tensile tests and shall conform to required values of tensile strength, yield point, and elongation.
  • ASTM A283 Chemical Properties
  Grade A Grade B Grade C Grade D
Carbon, max 0.14 0.17 0.24 0.27
Manganese, max 0.90 0.90 0.90 0.90
Phosphorus, max 0.035 0.035 0.035 0.035
Sulphur, max 0.04 0.04 0.04 0.04

Silicon

Plates 1 1/2 in and under, max

Plates over 1 1/2 in

0.40 0.15-0.40 0.40 0.15-0.40 0.40 0.15-0.40 0.40 0.15-0.40
Copper min % when copper steel is specified 0.20 0.20 0.20 0.20
  • ASTM A283 Mechanical Properties
  Grade A Grade B Grade C Grade D
Tensile Strength:

45,000 -60,000 psi

[310 - 415 MPa]

50,000 -65,000 psi

[345 - 450 MPa]

55,000 75,000 psi

[380 - 515 MPa]

60,000 -80,000 psi

[415 - 550 MPa]

Min. Yield Point:

24,000psi

[165 MPa]

27,000psi

[185 MPa]

30,000psi

[205 MPa]

33,000psi [

230 MPa]

Elongation in 8": 27% min 25% min 22% min 20% min
Elongation in 2": 38% min 28% min 25% min 23% min
  • ASTM A283 carbon steel is an alloy of iron, further classified as a carbon steel. This is steel specification covers four grades of low carbon steel plates of structural quality for general application. Grades A, B, C and D.