• Wuxi Jinlai Mechanical Processing Co., Ltd.
    John Fairbank
    stainless steel strip with good quality and the Sales clerk service is very good.i like this company i hope can work with your again
  • Wuxi Jinlai Mechanical Processing Co., Ltd.
    Fleuriau
    Shipment speed is very fast, and the requirements can meet me. Salesman is very responsible.
  • Wuxi Jinlai Mechanical Processing Co., Ltd.
    Fierce Urchin
    good ,the galvanized steel coil quality is good and i donot see the broken on them.that is nice
Contact Person : Jo Yuan
Phone Number : +86-18706170710
WhatsApp : +8618706170710

Low Carbon Mild Steel Sheet Manganese Containing Excellent Machinability

Place of Origin: China
Brand Name: JIN LAI
Certification: ISO BV
Model Number: A572 Grade 50
Minimum Order Quantity: 1 ton
Price: negotiation
Packaging Details: standard packing or as the requirement
Delivery Time: ship withon 10 days after receive the advance
Payment Terms: T/T, Western Union
Supply Ability: 5000 tons per month
Product Details
Length: 4-11M OR As Requirement Surface: Oil,black,galvanized
Packing: Standard Seaport Packing Width: 1000-2200mm
Standard: AISI, ASTM, BS, DIN, GB, JIS Material: C22 C25 C30 C35
Thickness: 1.5-380mm Technique: Hot Rolled
High Light:

cold rolled mild steel sheet

,

low carbon steel plate

Leave a Message
Product Description

The plates are made up of the excellent quality alloys that have great forming and welding properties. Plus, they are energy efficient and have the ability to payload higher therefore it is widely used in the linear structures. Some of the common applications where EN 10025-2 S690QL Tempered and Quenched Plate, is largely used are heavy transportation, lifting equipment, machine building, etc. On the other hand, some of the popular industries where it is used are petrochemical industries, chemical industries, fertilizer industries, power generation industries, nuclear industries, etc. The features offered by these amazing plates are- higher reliability, higher weldability capacity, easy to install in several small and big industries, easy to fabricate, excellent formability, toughness, it is a strong plate that can e utilized in the higher as well lower temperature conditions.

 

EN 10025-2 S690QL Steel PLATES higher strengthening properties and produces higher tensile, higher mechanical strength as well as higher-yielding strength when used in the different applications around the world. It also excites great resistance properties and some of them are corrosion resistance, oxidation resistance, pitting and crevice resistance, stress chloride cracking resistance, and many more. At Conquest Steel & Alloys we pack our product with higher quality packing substance in order to avoid any damage to the products. Additionally, we also conduct tests on them such as macro tests, hardness tests, micro tests, destructive tests, PMI tests, etc.

EN 10025-2 S690QL Steel Plate Specification :

Specification : ASTM A514/A514M-13
Item : EN 10025-2 S690QL Quenched And Tempered Structural Steel Plate
Thickness : 3 - 200mm
Width : 500 - 3000mm

Length : 1000 - 12000mm


 

EN 10025-2 S690QL STRUCTURAL STEEL PLATE EQUIVALENT GRADES

Grade Standards Country
S690QL EN10137-2 EN10025-6:2004 EN EUROPE
A709-100 ASTM USA
TStE690V DILLIMAX 690 NAXTRA 70 DIN, WNr GERMANY
E690T E690TFP S690T AFNOR/ NF A36- 204 FRANCE
FeE690VKT EN EUROPEAN (OLD)
2625 WELDOX 700 SS SWEDON
E690 ISO 4952 INTER
JFE HITEN 780LE JIS JAPAN
ALFORM 700   AUSTRIA

 

EN 10025-2 S690QL TEMPERED AND QUENCHED PLATE CHEMICAL COMPOSITION

C Si Mn P S B Cr Cu Mo N Nb* Ni Ti* V* Zr*
0.20 0.80 1.70 0.020 0.010 0.005 1.50 0.50 0.70 0.015 0.06 2.0 0.05 0.12 0.15

 

EN 10025-2 S690QL HIGH YIELD STRENGTH STEEL PLATES MECHANICAL PROPERTIES

Steel grade Yield strength ReH MPa Tensile strength Rm MPa EN 10025­6: 2004 + A1:2009 Heavy plate thickness mm Obsolete standard EN 10137­2 1995 Elongation,
min %
S690Q, QL 690 770 – 940 S690QL 6 – 60 S690QL 14

 

EN10025-2 S235J0

Chemical composition % MAX
THICKNESS(MM) C Mn Si P S N Cu
≦40 0.17 1.4 ~ 0.03 0.03 0.012 0.55
>40 0.17
Mechanical properties MIN
  Yield Strength MPa Tensile Strength MPa Elongation in 2 in. %
≦16 235 360-510 17
>16, ≦100 225
>100 175 340-500

 

EN10025-2 S235JR

Chemical composition % MAX
THICKNESS(MM) C Mn Si P S N Cu
≦40 0.17 1.4 ~ 0.035 0.035 0.012 0.55
>40 0.20
Mechanical properties MIN
  Yield Strength MPa Tensile Strength MPa Elongation in 2 in. %
≦16 235 360-510 17
>16, ≦100 215
>100 175 340-500

 

EN10025-2 S275JR

Chemical composition % MAX
THICKNESS(MM) C Mn Si P S N Cu
≦40 0.21 1.5 ~ 0.035 0.035 0.012 0.55
>40 0.22
Mechanical properties MIN
  Yield Strength MPa Tensile Strength MPa Elongation in 2 in. %
≦16 275 410-580 15
>16, ≦100 235
>100 205 380-540

 

EN10025-2 S235J2

Chemical composition % MAX
THICKNESS(MM) C Mn Si P S N Cu
≦40 0.17 1.4 ~ 0.025 0.025 ~ 0.55
>40 0.17
Mechanical properties MIN
  Yield Strength MPa Tensile Strength MPa Elongation in 2 in. %
≦16 235 360-510 15
>16, ≦100 225
>100 165 330-510

 

EN10025-2 S275J2

Chemical composition % MAX
THICKNESS(MM) C Mn0 Si P S N Cu
≦40 0.18 1.5 ~ 0.025 0.025 0.012 0.55
>40 0.18
Mechanical properties MIN
  Yield Strength MPa Tensile Strength MPa Elongation in 2 in. %
≦16 275 410-580 13
>16, ≦100 235
>100 195 410-580

 

EN10025-2 S275J0

Chemical composition % MAX
THICKNESS(MM) C Mn Si P S N Cu
≦40 0.18 1.5 ~ 0.03 0.03 0.012 0.55
>40 0.18
Mechanical properties MIN
  Yield Strength MPa Tensile Strength MPa Elongation in 2 in. %
≦16 275 410-580 15
>16, ≦100 235
>100 205 380-540

 

EN10025-2 S355J0

Chemical composition % MAX
THICKNESS(MM) C Mn Si P S N Cu
≦40 0.20 1.6 0.55 0.03 0.03 0.012 0.55
>40 0.22
Mechanical properties MIN
  Yield Strength MPa Tensile Strength MPa Elongation in 2 in. %
≦16 355 470-680 14
>16, ≦100 315
>100 275 450-600

 

EN10025-2 S355K2

Chemical composition % MAX
THICKNESS(MM) C Mn Si P S N Cu
≦40 0.20 1.6 0.55 0.025 0.025 ~ 0.55
>40 0.22
Mechanical properties MIN
  Yield Strength MPa Tensile Strength MPa Elongation in 2 in. %
≦16 355 470-680 12
>16, ≦100 315
>100 265 450-600

 

EN10025-2 S355J2

Chemical composition % MAX
THICKNESS(MM) C Mn Si P S N Cu
≦40 0.20 1.6 0.55 0.025 0.025 ~ 0.55
>40 0.22
Mechanical properties MIN
  Yield Strength MPa Tensile Strength MPa Elongation in 2 in. %
≦16 355 470-680 14
>16, ≦100 315
>100 265 450-600

 

EN10025-2 S420J0

Chemical composition % MAX
THICKNESS(MM) C Mn Si P S N Cu
≦40 0.20 1.7 0.55 0.03 0.03 0.025 0.55
>40 0.22
Mechanical properties MIN
  Yield Strength MPa Tensile Strength MPa Elongation in 2 in. %
≦16 450 550-720 17
>16, ≦100 410
>100 380 530-700